Appelkilic2033

Repair of critical size bone defects is a clinical challenge that usually necessitates the use of bone substitutes. For successful bone repair, the substitute should possess osteoconductive, osteoinductive, and vascularization potential, with the ability to control post-implantation infection serving as an additional advantage. With an aim to develop one such substitute, we optimized a zinc-doped hydroxyapatite (HapZ) nanocomposite decorated on reduced graphene oxide (rGO), termed as G3HapZ, and demonstrated its potential to augment the bone repair. The biocompatible composite displayed its osteoconductive potential in biomineralization studies, and its osteoinductive property was confirmed by its ability to induce mesenchymal stem cell (MSC) differentiation to osteogenic lineage assessed by in vitro mineralization (Alizarin red staining) and expression of osteogenic markers including runt-related transcription factor 2 (RUNX-2), alkaline phosphatase (ALP), type 1 collagen (COL1), bone morphogenic protein-2 (BMP-2), osteocalcin (OCN), and osteopontin (OPN). While the potential of G3HapZ to support vascularization was displayed by its ability to induce endothelial cell migration, attachment, and proliferation, its antimicrobial activity was confirmed using S. aureus. Biocompatibility of G3HapZ was demonstrated by its ability to induce bone regeneration and neovascularization in vivo. These results suggest that G3HapZ nanocomposites can be exploited for a range of strategies in developing orthopedic bone grafts to accelerate bone regeneration.Detection of slight changes in the chemical, thermal, and physical environments of the ocular surface is necessary to protect eyesight. The cornea, as the most densely innervated peripheral tissue in the body, can be damaged as a result of caustic chemical exposure. Such damage can be painful and debilitating, thus underscoring the need to understand mechanisms of ocular irritation. Both ethical and translational limitations regarding the use of animal subjects in part drive the need to develop relevant in vitro cell and tissue models that emulate the physiology of the human cornea. In this study, we utilized our 3D in vitro cornea-like tissue model to study the effects of irritation mediated by transient receptor potential (TRP) channels vanilloid 1 and ankyrin 1 (TRPV1; TRPA1) in response to allyl isothiocyanate (AITC) stimulation. Changes in gene expression were analyzed to characterize wound healing responses of the epithelial, stromal, and neuronal cell populations in the corneal tissue models. Key findings of the study include indications of wound healing, such as stromal myofibroblast differentiation and epithelial barrier re-establishment, amplification of pro-inflammatory cytokines, and downstream ECM protein remodeling due to irritation with the addition of sensory innervation. This study further establishes this in vitro tissue model as a useful tool for studying corneal irritation in vitro in a holistic manner with promise as a novel and sensitive tool for studying chemical exposures and subsequent responses.Carbonized iodine-doped particles (CIPs) were developed to overcome the disadvantages of computed tomography (CT) contrast agents, such as high osmolality and the radiodensity dilution of monomolecular contrast agents and low solubility and high toxicity of polymeric contrast agents. The CIPs were synthesized via a hydrothermal synthesis for 8 h using ATIPA (5-amino-2,4,6-triiodoisophthalic acid), glycerol, and tromethamine in the presence of D.W. (deionized water)-insoluble ATIPA converted into CIPs through a hydrothermal synthesis, showing high solubility and low osmotic pressure. The in vitro contrast effect determined for the resulting CIPs demonstrated a 57.6% enhancement compared to iohexol, and the osmotic pressure of the resulting CIPs was lower than that of iohexol. In addition, the CIPs demonstrated no dilution-induced contrast decrease in plasma and, therefore, demonstrated high contrast strength in vivo. Cytotoxicity tests, hemolysis assays, and histological analyses were conducted to verify the biocompatibility of the CIP product; however, no toxicity was observed. Furthermore, the CIP demonstrated a much higher contrast effect than iohexol at low concentrations. These results indicate that the CIP we have produced may be used as an effective blood pool agent for CT imaging.Thermoresponsive polymers (TRP)s have been widely used for various applications from controlling membrane fouling in separation to cell/cell sheet harvesting in regenerative medicine. While poly(N-isopropylacrylamide) (pNIPAAm) is the most commonly used TRP, less expensive and easily processed poly(vinyl methyl ether) (PVME) also shows a hydrophilic to hydrophobic transition at 32-35 °C, near physiological conditions. In this study, we investigated the processing conditions for retaining a stable layer of PVME thin film on silica surfaces via entrapment in a 3-aminopropyltriethoxysilane (APTES) network. In addition, the thermoresponsive behaviors (TRB) of the retained PVME films were evaluated. Blend thin films of PVME/APTES with 9010 and 5050 mass ratios were spin-coated from their solutions in ethanol under ambient conditions and then annealed in a vacuum oven at 40, 60, 80, or 120 °C for 1, 2, or 3 days. The annealed films were then thoroughly rinsed with room temperature water and then soaked in water for 3 days. Our results showed that annealing at a temperature of ≥40 °C was necessary for retaining a PVME film on the surface. Cloperastine fendizoate mw The higher annealing temperature led to greater film retention, probably due to the formation of a tighter APTES network. Regardless of processing conditions, all retained PVME films showed TRB, determined by water contact angles below and above the transition temperature of PVME. Additionally, particle attachment and protein adsorption on retained PVME films showed lower attachment or adsorption at room temperature as compared to that at 37 °C, and a greater difference was observed for the 9010 blend where more PVME was consisted. Furthermore, human mesenchymal stem cells attached and proliferated on the retained PVME surfaces at 37 °C and rapidly detached at room temperature. These results illustrated the potential applications of PVME surfaces as thermoresponsive supports for low-fouling applications and noninvasive cell harvesting.